QL-PP3015-W

Product model :QL-PP3015-W
Product description
PP release film is based on PP as a substrate, coated with silicon on one side to form the basic structure of the product
Polypropylene film with silicon release agent
Product characteristics
"QL-PP3015-W" is a PE release material developed by coating silicon release agent on the original film blown by polyethylene particles at high temperature. The product features stable release force and high cleanliness. It is suitable for all kinds of substrate free tape die cutting, foam die cutting frame rubber die cutting, rubber surface protection of daily chemical supplies and protection in various processes.
Product application range
Die-cutting protection for foam, conductive cloth, single-sided adhesive, double-sided adhesive, daily chemical supplies and other products.
Physical parameter
Class unit characteristic value test method
Color/White visual
Thickness um 30 5 thickness gauge
Adhesive/silicon release agent /
Peeling force gf/25mm 1-5g peeling force tester
Temperature test 60℃/1H C/1H high temperature oven
Fracture elongation % / tensile testing machine
Tensile strength Mpa/25mm/tensile testing machine
Surface fog, flat, no dirt
Product instructions
* Please clean up oil, water, dust and other impurities on the surface of the coated material before use.
* The above technical information is the company adopts the industry recognized reliable inspection method, does not do product specification guarantee
* When the processing conditions are strict, please test repeatedly and fully verify before use.
* The best storage condition of the product is 23 ℃, 50 ℃ 10%RH, shelf life is 6 months.
* Direct sunlight, high temperature (above 35℃), high humidity (above 70%RH), low temperature and other conditions are not guaranteed for 6 months.
* The surface of the object is damp, or dust, acid and alkali environment, and special materials can be put into use after repeated verification.
* The above data is for reference only and does not provide any guarantee of legal validity.